S. Syaripuddin, S. Sopiyan, S. Aditya, S.D. Yudanto, F.B. Susetyo
Enhance the surface hardness of materials usually conducted through a hardfacing technique. Hardfacing is popular, whereby materials with better properties are deposited over cheaper bulk material. This work fabricated hard layers by adding titanium (Ti) wire during the welding process. This research used low-carbon steel as the base material, wire optime Ti grade 1 for Ti addition, and an HV 600 electrode with a diameter of 3.2 mm for filler metal. A single-layer weld was conducted with SMAW (positive polarity and 90 A). The samples were directly quenched in a different solution after welding. The properties of the weld layer were examined phase, structure, microstructure, macrostructure, and hardness using optical emission spectroscopy (OES), x-ray diffraction (XRD), an optical microscope, a digital camera, and a hardness device, respectively. Adding titanium (Ti) to the weld layer and quenching the samples after welding in the solution enhances the hardness. This phenomenon is attributed to different phase compositions, oxides, and microstructures. A fine dispersion of small particles and oxide amount is important in increasing hardness. There is no cracking in the weld and base metal. In conclusion, samples BNTiO and BNTiM are recommended for lathe-cutting tools. © 2023 Materials and Energy Research Center. All rights reserved.
Department of Mechanical Engineering, Universitas Negeri Jakarta, Jakarta, Indonesia; Research Center for Metallurgy - National Research and Innovation Agency, Serpong, Indonesia
Research at a Glance
Register to unlock
Topics & SDG Alignment
Register to unlock
Collaboration
Register to unlock
Author Profile (Selected)
Register to unlock
References Overview
Register to unlock
Journal & Source
Register to unlock
Metadata & Integrity
Register to unlock