M. N. Abd Rahman, N.H. Zulkipli, M.S. Kasim, M.R. Jamli, E. Budi
Metal inert gas (MIG) welding technique is one of the most widely utilized permanent metal joining technique in various applications due to its adaptability towards automation. One of the critical process parameters in MIG is shielding gas flow rate. One of the main purposes of shielding gas is to prevent the formation of oxidation and porosity at the weld pool. However, study on the optimum level of shielding gas flow rate is lacking. This study investigated the impact of argon gas flow rate, as a shielding gas, on the weld zone hardness of a 3 mm thick mild steel plate. The flow rates of argon shielding gas were evaluated at five levels (0 SCFH, 15 SCFH, 30 SCFH, 45 SCFH, and 60 SCFH). Vickers hardness test was performed and an optical micrograph was captured for all samples. One-way ANOVA analysis was conducted to ascertain the statistical difference of hardness among the samples at a 95% confidence level. The results indicated that the argon flow rate has a significant positive impact on the hardness of the weld zones as the shielding gas flow rate increases from 0 to 45 SCFH. However, the hardness significantly dropped at 65 SCFH. The drop in hardness was attributed to an increase in the presence of porosity. It is postulated that the high shielding gas flow rate resulted in turbulence flow that promotes air entrapment in the weld joint during solidification. The high flow rate also induced rapidsolidification of weld joint that reduces the chance of air escaping from the weld pool. © 2022. Journal of Advanced Manufacturing Technology. All Rights Reserved.
Faculty of Manufacturing Engineering, Universiti Teknikal Malaysia Melaka, Malaysia; Advanced Manufacturing Centre, Universiti Teknikal Malaysia Melaka, Malaysia; Faculty of Mathematics and Science, Universitas Negeri Jakarta, Indonesia
Research at a Glance
Register to unlock
Topics & SDG Alignment
Register to unlock
Collaboration
Register to unlock
Author Profile (Selected)
Register to unlock
References Overview
Register to unlock
Journal & Source
Register to unlock
Metadata & Integrity
Register to unlock