Ansel Fabianta Tambunan, Irene Angela, Imam Basori, Bondan Tiara Sofyan
The microstructures, mechanical properties, deformation mechanism, and recrystallization behavior of Cu-Zn-Bi alloys for cartridge case application have been investigated in this research. Cu-28Zn-1.1Bi wt. % alloys were produced by gravity casting and subjected to a homogenization – cold rolling – annealing sequences with variations on reduction level and annealing temperature. Samples characterizations were done through optical emission spectroscopy, optical microscopy, SEM-EDS imaging, and X-ray mapping modes, while hardness measurements were performed using micro Vickers method. The presence of Bi was found to increase cartridge brass hardness through a dispersoid strengthening mechanism in which dislocation movements are rendered by Bi particles. Higher deformation levels resulted in higher microhardness of the alloy. Recrystallization took place at grain boundaries and areas surrounding Bi dispersoid at 400 °C, while further heating resulted in grain growth phenomenon. Bismuth addition accelerated the recrystallization process in cartridge brass by a particles stimulated nucleation (PSN) mechanism. © 2018 Trans Tech Publications, Switzerland.
Department of Metallurgy and Materials, Faculty of Engineering, Universitas Indonesia, Kampus UI, Depok, 16424, Indonesia; Department of Mechanical Engineering, Faculty of Engineering, Universitas Negeri Jakarta, Jl. Rawamangun Muka, Jakarta, 13220, Indonesia
Research at a Glance
Register to unlock
Topics & SDG Alignment
Register to unlock
Collaboration
Register to unlock
Author Profile (Selected)
Register to unlock
References Overview
Register to unlock
Journal & Source
Register to unlock
Metadata & Integrity
Register to unlock